KTiOPO4 (KTP) isan excellent nonlinear optical material and has been extensively used in frequency doubling of IR lasers. The 1064nm SHG conversion efficiency was reported high up to 80%. It has a lot of excellent properties such as high nonlinear optical coefficient (about 15 times KDP crystal), high Electro-Optic coefficient, low dielectric constant, high thermal conductivity (2 times that of BNN crystal ). In addition, KTP crystal is moisture free and mechanically stable. It has minimum mismatch gradient, super-polished optical surface and no decomposition below 900℃.

At 2000,INNOWIT have first developed the high-quality Super-KTP (S-KTP) . Its damage threshold is more than normal KTP.

Applications: 
◇ Frequency Doubling (SHG) of Nd-doped Lasers for Green/Red Light Generation. 
◇ Frequency Mixing (SFM) of Nd Laser and Diode Laser for Blue Light Generation . 
◇ Parametric Sources (OPG, OPA and OPO) for 0.6um-4.5um Tunable output. 
◇ E-O Modulators, Optical Switches, Directional Couplers. 
◇ Optical Waveguides for Integrated NLO and E-O Devices, etc. 
◇ PPKTP for device engineering etc.

INNOWIT'S warranty: 
◇ Standard size of KTP crystals for DPSS application; 
◇ AR-Coating, Mounting and Re-polishing Service; 
◇ Mass Production to Support Industrial and Commercial Applications; 
◇ Strict Quality Control; 
◇ Free Technical Support; 
◇ 1 - 3 Weeks Delivery ; 
◇ Attractive Price and quantity discount;

INNOWIT's specifications of KTP

Dimension tolerance:

±0.1mm

Flatness:

λ/8 @633nm

Scratch/Dig:

10/5(MIL-PRF-13830B)

Parallelism

better than 20 arc sec

Perpendicularity:

better than 5 arc min

Angle tolerance:

<± 0.2°

Coating:

AR coating

Residual reflectivity:

R1064<0.2% ,R532<0.5%,R1570<0.2%

Clear aperture:

>90% central area

Transmitting wavefront distortion:

less than λ/8 @633nm

  • 上一篇:没有了
  • 下一篇:KTA晶体
产品展示

华特中心

电话:0531-85198090
传真:0531-85198080
邮箱:wit@ahyztz.com

老虎机华特 | 新闻中心 | 国际文化 | 产品展示 | 人力资源 | 公司邮箱
鲁ICP备11003939号 | 鲁公网安备 37010202002000号
版权所有:山东苹果华特科技股份有限公司
威廉希尔的官方网址千亿国际娱乐网站龙8国际官方网站苹果手机版home–必发bf88官方唯一登陆